1) carbon-bearing pellet
含碳球团矿
2) carbon-containing chromite pellet
含碳铬矿球团
1.
Aimed at production of hot metal containing Cr from 20% to 40%, the carbon-containing chromite pellets made from three kinds of typical chromite were reduced at 1300 ℃ for 30 minutes and then melted at 1550~1600 ℃ for 10 minutes and the slag was separated.
以3种典型的铬矿为原料,生产铬的质量分数为20%～40%的铁水为目标,对含碳铬矿球团在1300℃温度下还原30min,然后在1550～1600℃温度下恒温10min,进行渣金分离。
3) Carbon-bearing Iron Ore Pellets
含碳铁矿球团
4) carbon-containing chromite briquette
含碳铬铁矿球团
5) carbon contained pellets
含碳团矿
1.
Experimental studies on direct reduction of carbon contained pellets were performed under the carbon covered protective condition and open fired atmosphere.
在盖碳保护敞焰加热条件下，对含碳团矿进行试验研究，得到金属化率与加热时间、加热温度、料层厚度等参数间的定量关系，从而确定了球团还原时获得高金属化率的条件。
6) carbon-bearing pellet
含碳球团
1.
Under the condition of 1000~1200 ℃,study the effect of the carbon-bearing pellet strengths and metallization rate with different iron ore concentrate size,matching carbon ratio(carbon oxygen mol ratio),kind of additive and reduction temperature.
在1000～1200℃条件下研究了不同的矿粉粒度、配碳比、粘结剂、还原温度等对含碳球团强度及金属化率的影响。
2.
The carbon-bearing pellets made of zinc-bearing dust and sludge,iron concentrates and additive of agglomerant were reduced at 1 000~1 200 °C,the effects of different kinds of additive and reduction temperature on the strength and metallization rate of carbon-bearing pellets were studied.
将含锌尘泥、铁精矿及粘结剂混合造成的含碳球团在1050~1250℃条件下还原,研究了不同粘结剂、不同温度对其强度及金属化率的影响。
3.
A new technique that layer of carbon-bearing pellets is heated and direct reduced under conditon of parallel-flow heating with pre- heated air is put forword.
提出了一种顺流加热含碳球团直接还原的新方法。
补充资料：球团矿
球团矿
pellet
q一utuankuang球团矿(pellet)将细粒度的铁精矿配入少量球团私结剂，经过造球与焙烧制成的球状炉料。它和烧结矿并称为人造富矿。主要作为高炉炼铁的原料，也可以作为直接还原铁及熔融还原铁的原料，在炼钢过程中可作为氧化剂及冷却剂使用。 类别球团矿按化学成分主要有酸性球团矿和自熔性球团矿两大类。酸性球团矿的主要矿物为赤铁矿，脉石成分以酸性的510:为主，含碱性物质cao，MgO极少;自熔性球团矿的主要矿物为赤铁矿，脉石成分除510:外含有较多的CaO，碱度(CaO/510。)一般在0.8一1.2之间。此外为了改善球团矿的高温冶金性能，在球团原料中添加橄榄石、白云石、煤或预还原处理，分别获得橄榄石球团矿、白云石球团矿，多孔球团矿和预还原球团矿。球团矿按其固结方式可分为焙烧固结球团矿和冷固结球团矿。前者在高温下(1200一1300℃)以Fe203的再结晶与晶粒长大使球团矿具有很高的强度，后者以各种豁结剂把铁精矿固结起来，如水玻璃、腐殖酸钠、纸浆废液、膨润土等，或者以细磨的高炉水、渣、波特兰水泥、消石灰等形成水化硅酸盐的微晶，使球团矿具有一定的强度。世界上90%以上的球团矿是高温焙烧固结的。 性能球团矿的强度高(单个球的抗压强度达Z000N以上)，转鼓指数可达95%(150标准)，可以长期贮存和长途运输，它的粒度均匀(一般为9一12.smm)，颗粒间孔隙度大，透气性好。球团矿的气孔率高(2。%以上)，且多为均匀分布的开口微气孔，加之主要矿物为赤铁矿，故还原性好。球团矿在氧化性气氛下焙烧，因而兼有除硫作用，一般球团矿含硫很低。由于球团矿不是依靠液相来固结的，可以使用含铁量很高的铁精矿作为原料，生产出品位高、杂质少的优质人造富矿。 (孔令坛)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。