1) multielement V-Ti nodular graphite cast iron
多元素钒钛球墨铸铁
1.
It proves here that multielement V-Ti nodular graphite cast iron is an excellent material for piston rings worthwhile spreading its application.
介绍了多元素钒钛球墨铸铁活塞环磨损机理、铸造工艺、综合性能、物化性质、金相组织概况及该产品装机工况和台架快磨试验结果,阐述了多元素钒钛球墨铸铁是一种值得推广应用的新型优质活塞环材质。
2) Multi-Element V-Ti Nodular Cast Iron
多元素钒球墨铸铁
3) VTi cast iron
钒钛铸铁
1.
Laser strengthening process and structure characteristics of VTi cast iron cylinder liners in diesel engine are discussed in this paper.
论述了钒钛铸铁柴油机缸套激光强化的工艺与组织特征。
4) Ferrite ductile iron
铁素体球墨铸铁
1.
Based on analysis of the chemical composition, nodular process and treated process influencing ferrite ductile iron are analyzed.
对影响铁素体球墨铸铁的化学成份、球化、孕育处理等因素进行分析。
5) as-cast ferrite nodular iron
铸态铁素体球墨铸铁
1.
The quality control of cored-wire injection process used for production of as-cast ferrite nodular iron was described.
介绍用喂线球化工艺生产优质铸态铁素体球墨铸铁的质量控制要点。
6) nodular cast iron
球墨铸铁
1.
Study on wind cooling strengthening process of nodular cast iron;
低牌号球墨铸铁风冷强化工艺的试验研究
2.
Analysis and Prevention About Graphite Blooming of the Nodular Cast Iron;
球墨铸铁石墨开花问题的分析与防范
3.
Harrow Piece of Nodular Cast Iron in Squeezing Casting;
球墨铸铁耙片挤压铸造新工艺
补充资料：球墨铸铁
析出的石墨呈球形的铸铁。球状石墨对金属基体的割裂作用比片状石墨小，使铸铁的强度达到基体组织强度的70～90％，抗拉强度可达120kgf/mm2，并且具有良好的韧性。球墨铸铁除铁外的化学成分通常为：含碳量3.6～3.8％，含硅量2.0～3.0％，含锰、磷、硫总量不超过1.5％和适量的稀土、镁等球化剂。
球墨铸铁生产工艺简单，铸造性能比铸钢好（但比灰口铸铁差），成本低，因此，被广泛用来制作受力复杂，对强度和韧性以及耐磨性要求较高的零件，如曲轴、齿轮、高压缸、汽车底盘零件等。20世纪70年代全世界的球墨铸铁管的年产量达数百万吨。中国古代铸铁中亦有球状石墨的组织（见冶金史）。
球墨铸铁生产工艺简单，铸造性能比铸钢好（但比灰口铸铁差），成本低，因此，被广泛用来制作受力复杂，对强度和韧性以及耐磨性要求较高的零件，如曲轴、齿轮、高压缸、汽车底盘零件等。20世纪70年代全世界的球墨铸铁管的年产量达数百万吨。中国古代铸铁中亦有球状石墨的组织（见冶金史）。