1.
The results of microscope,SEM,TEM and EDS revealed that the particles precipitated in the pre- austenite grain boundaries will result in network cracks under sufficient stress such as thermal stress,bending and straightening stress due to uneven cooling of strand surface.
采用金相显微镜、SEM、TEM和EDS等方法,分析了因连铸板坯表面冷却不均匀引起γ→α反复相变导致碳氮化物在晶界析出,并在外力(热应力、弯曲矫直应力等)作用下产生沿晶界开裂的网状裂纹的形成机理,以及钢中[C]、Mn/S、[Al]、[V]、连铸冷却强度等对连铸板坯网状裂纹的形成和扩展的影响。
2.
For the surface network cracks in 200mm thickness slabs for pipeline and veicle frame,it is found that the carbon content,Mn/S ratio and Al,Ti,V,Nb alloy additions and continuous caster conditions are attributa- ble to the formation and propagation of surface and subsurface network cracks.
统计分析了攀钢所产管线钢、梁板钢等200mm×1300mm连铸坯表层网状裂纹的影响因素;发现钢中碳、锰硫比、合金元素(Al,Ti,V)、连铸机设备和浇注状况对其形成和扩展都有重要影响。
3.
For the surface network cracks in 200mm thickness slabs for pipeline and vehicle frame, it is found that the carbon content,Mn/S ratio and Al,Ti,V,Nb alloy additions and continuous caster conditions are attributable to the formation and propagation of surface and subsurface network cracks.
针对攀钢生产的管线钢、梁板钢等200×1300mm~2连铸坯表层出现网状裂纹,对其影响因素进行统计分析,发现钢中C、Mn／S 比和 Al、Ti、V、Nb 等合金元素及连铸机设备和浇注状况对连铸坯表层网状裂纹的形成和扩展都有重要影响。
6) Mesh crack
网状裂隙
补充资料：J形及L形密封
分子式：
CAS号：
性质：两种均为唇形橡胶密封，截面形状分别为J形和L形。多为纯橡胶制品，也有少数是夹布制品。根据使用条件，一般用天然橡胶或丁腈橡胶制造。结构较简单，摩擦力低，专用于气压或液压机械设备的活塞及活塞杆密封，工作压力在1MPa以下，如用于汽车和火车制动系统及离合器操纵系统中，起传递压力和密封的作用。
CAS号：
性质：两种均为唇形橡胶密封，截面形状分别为J形和L形。多为纯橡胶制品，也有少数是夹布制品。根据使用条件，一般用天然橡胶或丁腈橡胶制造。结构较简单，摩擦力低，专用于气压或液压机械设备的活塞及活塞杆密封，工作压力在1MPa以下，如用于汽车和火车制动系统及离合器操纵系统中，起传递压力和密封的作用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条