1) quadruple ceramics
四元系陶瓷
1.
The electric properties of Pb(Li 1/4 Nb 3/4 )O 3 Pb(Fe 1/3 Sb 2/3 ) PbTiO 3 PbZrO 3 quadruple ceramics with different proportions and dopants are investigated by analyzing piezoelectric properties, mechanic quality and the diffusive graph of relative dielectric constant vs temperature of different samples.
通过对几种不同的样品压电特性、机械品质因数和介电温谱等特性的对比和分析 ,研究了Pb (Li1/4Nb3 /4 )O3 Pb (Fe1/3 Sb2 /3 )O3 PbTiO3 PbZrO3 四元系陶瓷在不同配比和掺杂下的机电性能 ,发现该系列样品具有较高的压电常数 (可达 3 4 0× 10 -12 C/N)和介电驰豫温谱。
2) PMMN quaternary piezoelectric ceramic
PMMN四元系压电陶瓷
3) trinary system ceramics
三元系陶瓷
1.
The experimental results show that the trinary system ceramics is a promising candidate .
对ｘ Ｐｂ（ Ｙ１／２ Ｎｂ１／２ ） Ｏ３ｙ Ｐｂ Ｔｉ Ｏ３ｚ Ｐｂ Ｚｒ Ｏ３ 三元系陶瓷材料进行了研究，对其压电与介电性能进行了测量，发现该三元系材料在 ｘ＝ ０。
4) multiphase ceramics composites
多元系复相陶瓷
1.
The preparation technology of ZrO2 toughened A12O3-TiC multiphase ceramics composites and the effect of ZrO2 content on the properties of fracture toughness, bending strength, Vicker hardness of composites have been investigated in the paper.
本文通过对ZrO_3增韧Al_2O_3—TiC系复相陶瓷材料的制备工艺以及ZrO_2含量的变化对材料断裂韧性、抗弯强度以及硬度的影响研究,采用X射线衍射法分析断口相变量随组成变化对多元系复相陶瓷断裂韧性、抗弯强度的影响,同时分析在不同冲击工况下其耐冲蚀磨损特性与力学性能之间的关系。
5) quirnary system
五元系压电陶瓷
补充资料：低温钛酸钡系热敏陶瓷
分子式： BaTiO3
CAS号：
性质：居里温度120℃以下的热敏陶瓷。除主成分钛酸钡外，还含锶、铝、钇、硅等氧化物。材料常温电阻率低，一般为10～102Ω·cm，升阻比(电阻落差)大，为103～108，耐压特性高，电压特性低。电极采用化镀镍或铜后，表面再镀银或烧银方法制成，也可直接烧渗银锌制成欧姆接触电极。主要用于制作彩电消磁、马达启动、过流保护等元件。
CAS号：
性质：居里温度120℃以下的热敏陶瓷。除主成分钛酸钡外，还含锶、铝、钇、硅等氧化物。材料常温电阻率低，一般为10～102Ω·cm，升阻比(电阻落差)大，为103～108，耐压特性高，电压特性低。电极采用化镀镍或铜后，表面再镀银或烧银方法制成，也可直接烧渗银锌制成欧姆接触电极。主要用于制作彩电消磁、马达启动、过流保护等元件。