1) spinning and forming
纺丝成形
1.
The effects of total solid in dope,spinning temperature,temperature and concentration in coagulation bath,negative stretch of spinneret and spinning velocity on the performance of fiber were analyzed,which provided basis for selection of appropriate spinning and forming process.
利用改性聚合体,配制原液,从纺丝原液及纺丝成形加工工艺两方面,具体分析了原液总固、原供纺温度、凝固浴温度和浓度、喷丝头负拉伸、喷丝速度等对纤维性能的影响,为选择合适的纺丝成形工艺提供依据。
2) spinning formation model
纺丝成形模型
3) spun-laid
纺丝成网
1.
The article first introduces briefly the production principle and applications of spun-laid nonwoven fabric and then gives a detailed introduction to some key points in the installation of LW 402-320 (S) PP calender bonded nonwoven fabric production line developed and manufactured by Shaoyang Textile Machinery Works and sets forth personnel opinions on certain points to be noticed in production.
文章简要介绍了纺丝成网非织造布生产原理、用途。
4) To spin silk into yarn
纺丝成纱
5) spin texturing
纺丝变形
6) spunlaid technology
纺丝成网法
1.
It is used by spunlaid technology,extrusion forming and composite process to produce the composite fabric.
选择聚丙烯为纤维原料采用纺丝成网法制成吸声非织造布,以铜、铁粉末为主要隔声材料采用挤出成型工艺制成隔声片材,经化学粘合复合工艺研制出非织造降噪复合材料。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。