1) glass-based coating
玻璃基涂层
1.
To solve the severe oxidation problems of molybdenum at high temperature in air,a glass-based coating has been successfully developed to protect molybdenum electrodes from oxidation in the process of heating up kiln.
针对钼在高温下极易氧化的问题,开发了一种在烤窑时防止钼电极被氧化的玻璃基涂层。
2) glass based ceramic layer
玻璃基陶瓷涂层
3) glass coating
玻璃涂层
1.
The effects of processing parameters and adding rare earth on the corrosion resistance of glass coatings on metal surface were studied by means of electrochemical test, immersion test,pitting test and scanning electron microscope.
利用斑点试验、点蚀试验、电化学测试及扫描电镜等方法 ,研究了熔敷温度、保温时间和稀土添加量等工艺参数对热熔敷法制备的玻璃涂层耐蚀性的影响 ,探讨了添加稀土提高玻璃涂层耐蚀性的机理。
2.
The corrosion mechanism of flame sprayed glass coatings was studied in this paper.
研究了手工火焰喷涂玻璃涂层的腐蚀破坏机理。
3.
The impact test, the thermal shock test and the scanning electron microscopy were used to investigate the effect of rare earth oxide on the adhesiveness between the glass coating and the base metal.
利用冲击试验、热震试验和扫描电镜等方法研究了添加氧化铈对玻璃涂层与金属基体密着性的影响规律。
4) TiO 2 coated glass
TiO2涂层玻璃
5) glassy coating
玻璃质涂层
6) FRP coating
玻璃钢涂层
1.
In response to this question this issue designed and developed a new type of FRP coating composite materials, glass fiber materials powder was used as enhance m.
针对这一问题,本课题设计并研制了一种新型防腐玻璃钢涂层复合材料,其增强材料选用玻璃纤维粉而不是传统的玻璃纤维布或短切玻璃纤维,在保证传统玻璃钢优异的物理化学性能的同时,赋予了玻璃钢良好的涂覆流动性,施工时可以使用挤涂法将料浆直接涂敷在管道内壁上,形成玻璃钢涂层,室温下18小时内即可固化成型且成型质量好。
补充资料：双(2,3-环氧环戊基)醚玻璃布层合板
分子式：
CAS号：
性质：以双(2,3-环氧环戊基)醚为基料的层合板。马丁耐热270℃。拉伸强度371MPa。弯曲强度487MPa。冲击强度125kJ／m2。体积电阻率l.18×1015Ω·cm。将双(2,3-环氧环戊基)醚与固化剂等制成胶液或B阶树脂后,充分浸渍玻璃布,再叠层并层合即得。主要用作航空航天器材、电子元件和体育器材等。
CAS号：
性质：以双(2,3-环氧环戊基)醚为基料的层合板。马丁耐热270℃。拉伸强度371MPa。弯曲强度487MPa。冲击强度125kJ／m2。体积电阻率l.18×1015Ω·cm。将双(2,3-环氧环戊基)醚与固化剂等制成胶液或B阶树脂后,充分浸渍玻璃布,再叠层并层合即得。主要用作航空航天器材、电子元件和体育器材等。