1) fully-penetrated molten pool
全熔透熔池
1.
Based on the complete and correct equations of both top and back surfaces deformations of molten pool and the more accurately predicted weld pool geometry, the fully-penetrated molten pool surface deformation at the quasi-steady state were numerically calculated and discussed.
以完备的全熔透熔池上、下表面变形方程为基础,基于精度更高的熔池形状数值分析结果,计算和讨论了GTAW焊接不锈钢和低碳钢的焊接过程达到准稳态时熔池上表面和下表面的变形,并对计算结果给予了试验验证。
2) full-penetrated weldpool
熔透熔池
1.
The weld penetration extent was described by 3D information on the surface depression of full-penetrated weldpool.
利用所建立的TIG(钨极惰性气体保护电弧焊)焊接熔池形态瞬时行为的数学模型,对准稳态情况下当焊接工艺参数发生突变时熔透熔池表面下塌变形的动态演变过程进行了数值模拟,得出了指导焊接熔透控制系统设计的基础数据。
3) partial penetrated weld pool
未熔透熔池
1.
The qualitative analysis is carried out on the behavior of the partial penetrated weld pool with welding current changing from pulsed peak value to base value during pulsed TIG welding.
对脉冲TIG焊未熔透型熔池在脉冲峰 -基转换期间熔池三维形态变化行为进行了定性的分析 ,并从力和能量角度建立了未熔透熔池液面形态的数学模型。
4) full-penetration weld pool
TIG熔透熔池
5) full penetration
全熔透
1.
The shape regulations of full penetration for pulsed GMAG of thin plate were investigated, and some molten pool and weld bead characterized parameters for determining penetration were proposed based on the analysis of fusion metal volume.
文中分析了薄板脉冲熔化极气体保护焊(P-GMAW)全熔透过程的成形规律,从熔融金属体积量出发,提出了可以反映熔透的正面熔池及焊缝特征参量。
2.
Both monotonic axial compressive and axially loaded cyclic tests have been carried out on the steel box brace used in New CCTV Building to investigate the effect of assembling welds including full penetration and partial penetration on the structural behavior of the brace.
为考察全熔透和部分熔透两种组装焊缝形式对箱形截面钢支撑受力性能的影响,本文对中央电视台新台址建设工程中的箱形截面支撑进行了单调受压、轴向反复拉压试验;同时,采用ABAQUS有限元软件实现了对部分熔透试件未熔透处的接触模拟和滞回性能模拟。
3.
At present in China,one side full penetration welding of heavy plate are rarely designed and nealy no metal construction manufacture can satisfy this request without any defact after welding UT check.
目前国内设计很少应用大量的中、厚钢板单面焊全熔透焊缝,也几乎没有能够满足此种焊缝质量要求的金属结构件制作厂家,多数厂家即使是压力容器专业制造厂,在焊接此类焊缝时,也会存在不同程度的焊缝根部未熔合或未焊透,通过采取新型焊接工艺,反复试验,不断改进,最终保证了此类焊缝UT探伤时焊缝有效深度≥板厚,UT探伤一次合格率达90%以上,有效地保证了此类焊缝的焊接质量,同时也大大提高了生产效率。
6) complete fusion
完全熔化，熔透
补充资料：熔盐电解法生产铌粉(见熔盐电解法生产钽粉)
熔盐电解法生产铌粉(见熔盐电解法生产钽粉)
production of niobium powder by molten salt electrolysis
rongyand+onjlefa ShengChan n.fen熔盐电解法生产妮粉(produetion。fn;obi-um powder by molten salt eleetrolysls)见熔盐电解法生产担粉。