1) TiO2-SiO2 composite support
钛硅复合载体
2) TiO2-SiO2 composite oxide
钛硅复合氧化物
1.
The TiO2 and TiO2-SiO2 composite oxide were prepared by Sol-gel method and characterized by XRD,BET and DRS.
用溶胶-凝胶法制备了TiO2和钛硅复合氧化物,对样品进行了X射线衍射(XRD)、比表面积测试(BET)和紫外-可见漫反射光谱(DRS)分析,并以甲基橙为模拟污染物,考察了其光催化性能。
2.
Preparative methods of sol-gel,hydrolysis precipitation,hydrothermal synthesis for photocatalysts of TiO2-SiO2 composite oxide at home and abroad are introduced in this paper.
介绍了溶胶–凝胶法、水解沉淀法、水热合成法制备钛硅复合氧化物光催化剂的研究进展,评述了3种制备方法的优缺点以及添加硅对TiO2光催化活性的影响:添加硅后增大了催化剂的比表面积,提高了TiO2晶型转变温度,增强了其表面酸度,生成的Ti—O—Si键抑制了TiO2粒径的增大,拓宽了催化剂的禁带宽度,从而提高了光催化剂的催化活性。
3) titania-silica composite oxide
硅钛复合氧化物
1.
Bimodal porous titania-silica composite oxide were prepared via sol-gel method with an addition of nonionic surfactant C16EO10 as the structure-directing agent.
采用正硅酸甲酯和钛酸丁酯作为硅和钛的前驱体,在溶胶-凝胶过程中添加非离子表面活性剂C16EO10作为结构导向剂合成双孔结构硅钛复合氧化物材料。
4) organic Ti-Si compound material
钛-硅烷复合材料
5) composite support
复合载体
1.
Application of TiO_2-Al_2O_3 composite support on ultra deep hydrodesulfurization;
负载型TiO_2-Al_2O_3复合载体在超深度加氢脱硫中的应用
2.
A series of SiO2-Al2O3 composite supports were prepared by simple hydrolysis and deposition of Na2SiO3·9H2O on macropore Al2O3.
以硅酸钠为原料,以大孔Al2O3为基载体,采用水解沉积法制备了SiO2-Al2O3复合载体。
3.
The impregnation-precipitation method was adopted to prepare the nano-sized ZrO2/Al2O3 composite supports.
采用浸渍-沉淀法制备了负载型纳米ZrO2/Al2O3复合载体。
6) composite carrier
复合载体
1.
A series of Cu catalysts supported on MgO/Sepiolite composite carriers were prepared by precipitation method combined with impregnation method and used for dehydrogenation of cyclohexanol.
采用浸渍沉淀法制备了不同比例的MgO/海泡石(Sep)复合载体负载Cu催化剂,并考察了其对环己醇脱氢反应的催化性能。
2.
A composite carrier consisting of magnesium dichloride and polyethylene terephthalate (MgCl_2/PET) was prepared with emulsification method.
使用乳化法制备了一种新型的MgCl_2/聚对苯二甲酸乙二酯(PET)复合载体,用扫描电子显微镜、红外光谱仪、差示扫描量热仪-热重分析仪和X射线粉末衍射仪进行表征。
3.
Escherichia coli cells were immobilized with composite carriers of carrageenan and gelatin.
用卡拉胶与明胶复合载体固定大肠杆菌,优化了固定化细胞的制备条件,并利用该复合载体固定大肠杆菌细胞进行酶法制备γ-氨基丁酸的研究。
补充资料：氮化硅晶须补强碳化硅陶瓷复合材料
分子式：
CAS号：
性质：以碳化硅陶瓷为基体，以氮化硅晶须为增强体的复合材料。它既保留了碳化硅陶瓷优良的耐高温、抗蠕变、抗氧化、抗化学腐蚀、耐磨等性能，又具有比碳化硅陶瓷更高的强度和韧性，最高使用温度可达1400℃以上。由于氮化硅晶须与碳化硅陶瓷基体具有较好的物理相容性，化学性质相近，界面的结合力较强。该复合材料的烧结温度高，界面控制困难，成本高，主要用于航空、航天领域的高温部件。
CAS号：
性质：以碳化硅陶瓷为基体，以氮化硅晶须为增强体的复合材料。它既保留了碳化硅陶瓷优良的耐高温、抗蠕变、抗氧化、抗化学腐蚀、耐磨等性能，又具有比碳化硅陶瓷更高的强度和韧性，最高使用温度可达1400℃以上。由于氮化硅晶须与碳化硅陶瓷基体具有较好的物理相容性，化学性质相近，界面的结合力较强。该复合材料的烧结温度高，界面控制困难，成本高，主要用于航空、航天领域的高温部件。