1) Complex silicone rubber
复合型硅橡胶
2) composite PDMS membrane
硅橡胶复合膜
1.
Study on Perstraction with Composite PDMS Membrane;
硅橡胶复合膜渗透萃取研究
2.
In this work,the composite PDMS membrane was prepared to pervaporate Chinese rice wine and produce low-alcohol beverage at 40 ℃ and 260Pa downstream pressure.
在40℃,膜下游侧压力为260 Pa下,用自制的硅橡胶复合膜对传统黄酒进行了渗透汽化脱醇研究,重点对黄酒中10种主要风味物质和理化指标的变化进行了分析。
3) composite silicone rubber membrane
硅橡胶复合膜
1.
Effect of biomass on the pervaporation performance of composite silicone rubber membrane;
细胞对硅橡胶复合膜渗透蒸发分离性能的影响
2.
Pertraction mass transfer process of phenol from aqueous solution using composite silicone rubber membrane;
硅橡胶复合膜用于含酚水溶液渗透萃取传质过程
4) silicone rubber composite
硅橡胶复合材料
1.
Properties of silicone rubber composite filled with high-structured conductive carbon black;
高结构导电炭黑填充硅橡胶复合材料的性能
5) Silicon rubber compound bushing
硅橡胶复合套管
6) PDMS composite membrane
硅橡胶复合膜
1.
Study on preparation,pervaporation and separation performances of the PDMS composite membranes supported by polyester(PET)
聚酯(PET)硅橡胶复合膜制备与渗透汽化分离性能的研究
2.
The PDMS composite membrane was proved to be an promising membrane to separate ethanol and flavoring compositions from the broth.
采用苹果原汁发酵与渗透汽化膜分离相耦合的模式,在较低的温度下进行发酵,用硅橡胶复合膜将发酵液中的乙醇及其他挥发性香味成分选择性地分离出来,缩短了发酵周期,有效地避免了热敏性香味物质的损失。
补充资料：7001a/7001b型室温硫化硅橡胶
一、简介：
7001a/7001b系室温硫化型双组份硅橡胶，具有良好的流动性、消泡性，优异的耐臭氧、耐紫外光、耐老化性能和优良的电气绝缘性能。可在-60~200℃下长期使用。
二、常规性能：
测试项目 测试方法或条件 7001a 7001b
外 观 目 测 黑色粘稠液体 无色透明液体
粘 度 40℃ mpa·s 4000~5000 18~22
混合粘度 40℃ mpa·s 1000~2000 1000~2000
保存期限 室温通风 一年 一年
三、使用工艺：
项 目 单位或条件 7001a/7001b
混合比例 重量比 100:15
可使用时间 25℃，分钟 20
固化条件 ℃/hrs 25/24
四、用途：
适用于像素管、中小型电子元器件、电气及仪器仪表行业中的防潮、防霉、耐热绝缘的封装。
五、固化后特性：
项目 单位或条件 7001a/7001b
硬度 shore-a 20~40
体积电阻率 25℃，ω·cm 1.0×1013
绝缘强度 25℃，kv/mm >15
介电常数 25℃，1mhz 2.6~3.0
介质损耗角正切 25℃，1mhz <0.003
拉伸强度 kgf/mm2 0.5~1.5
相对伸长率 % 50~200
说明：补充资料仅用于学习参考，请勿用于其它任何用途。