Transformation mechanism of carbides and their effect on the stress rupture property were investigated in a Ni-base single crystal superalloy with microcontent of carbon.
015%)碳的镍基单晶高温合金在热处理和持久过程中的碳化物演化机制以及各种碳化物对合金持久性能的影响。
2.
The results show that no recrystallization occurs at 1050℃ but coarse γ′ phases precipitate and stress rupture property decreases.
对标准热处理后的第一代单晶高温合金DD3吹砂,然后采用不同温度进行热处理,研究了吹砂后热处理温度对合金1000℃/195 MPa持久性能的影响。
3.
Results showed that holding for such short time,there were a lot of blocky γ′phases in the bonding seam with D1P interlayer alloy,causing a lower stress rupture property of about 60% of.
对上述规范下获得的DD3接头组织和性能进行了研究分析,结果表明,扩散时间短,D1P中间层合金扩散焊接头组织很不均匀,在中间层合金流入处生成大量光板γ′相,对接头持久性能不利,1250℃下扩散4h接头的980℃持久性能为母材性能的60%;而D1F中间层合金扩散焊接头组织均匀一致,1250℃下扩散4h接头980℃持久性能超过母材性能的70%。
4) stress rupture
持久性能
1.
The effects of different heat-treatment on microstructure and stress rupture of MX246A have been studied in the present investigation.
研究了不同热处理制度对MX246A合金显微组织和持久性能的影响。
2.
It shows that this method can successfully predict the stress rupture of test alloy.
在Monkman-Grant方程的基础上计算了试验合金的Larson-Miller曲线,对预测的结果与试验结果进行了比较,计算曲线与实测曲线有较好的吻合,证明该方法能够准确地预测试验合金的持久性能。
3.
The influence of microstructure after long time aging at high temperature on the stress rupture at 1010℃/248MPa was investigated.
研究了高温长期时效对一种镍基单晶合金组织和在1010℃/248MPa条件下的持久性能的影响。
5) stress rupture properties
持久性能
1.
The microstructures and stress rupture properties of the second generation single crystal superalloy DD6 with [001] orientation were investigated after the full heat treatments were performed and aged at 980 ℃ for 100, 200, 300, 400, 600, 800 and 1000 h, respectively.
选用980℃时效温度、分别对[001]取向标准热处理后的第2代单晶高温合金DD6进行100,200,300,400,600,800及1000h的长期时效,研究了合金的显微组织与持久性能。
2.
The effects of low angle grain boundaries(LABs) on the stress rupture properties of second generation single crystal superalloy DD6 were investigated at 800℃,850℃ and 900℃.
在800℃,850℃和900℃的温度条件下,研究小角度晶界对第二代单晶高温合金DD6持久性能的影响。
3.
The effects of heat treatment on the microstructures and stress rupture properties for the single crystal Ni-base superalloy have been investigated.
研究了不同热处理工艺对一种镍基单晶高温合金的组织和持久性能的影响。
6) stress-rupture properties
持久性能
1.
However,the joints brazed with Co45CrNiWBSi filler metal bearing elements Si and B possessed poor stress-rupture properties,and the ones.
用Co45CrN iWBS i,Co45N iCrWB及N300E三种钴基钎料对定向凝固N i3A l基合金IC6A的真空钎焊进行探索研究,测定钎焊接头在900℃下的持久性能。
2.
The effect of delta-phase on stress-rupture properties of Alloy GH4169 is studied in this paper.
研究了δ相对ＧＨ４１６９合金持久性能的影响。
补充资料：发电能源在一次能源消费中的比重
发电能源在一次能源消费中的比重
the share of energy for electricity generation in total primary energy
fad旧n nengyuan za一y一ei nengyuan x.oofe一zhong由b lzhong发电能源在一次能派消费中的比，(theshare of energy for eleetrieity罗neratinn in totalprimary energy)是表征一个国家国民经济电气化程度的一个指标。在一次能源总消费中，发电用能源的比例越大，电力在能源系统中的地位越重要，国民经济电气化的程度就越高。由于使用电力比直接使用石油、天然气和煤炭等一次能源的效率高，且电力用途广泛，使用灵活方便，不污染环境，可靠性高，因此.世界各国的电力生产和消费以高于能源的速度增长，发电用能源在一次能源总消费t中的比例日益增大。下表列出了一些国家发电用能源占一次能源总消费的比例变化情况。一些日家发电能一占一次能派总消.一的比，(%)┌──┬───┬───┬──┬───┬──┬───┬───┐│年份│美国 │日本 │德国│加章大│法国│英国 │中国 │├──┼───┼───┼──┼───┼──┼───┼───┤│1970│28.4 │31。1 │ │43.3 │23.8│ │ │├──┼───┼───┼──┼───┼──┼───┼───┤│1980│37。65│44.9 │30.7│57.1 │36.1│39.7 │20.60 │├──┼───┼───┼──┼───┼──┼───┼───┤│1990│41.79 │50.30 │33.7│58.9 │46.0│37。6 │24.68 │├──┼───┼───┼──┼───┼──┼───┼───┤│1995│40.50 │51.50 │35.8│63.7 │57.0│36.7 │29.58 │├──┼───┼───┼──┼───┼──┼───┼───┤│1996│41。0 │50.7 │34.9│64。3 │54.2│35.4 │30.76 │└──┴───┴───┴──┴───┴──┴───┴───┘ 注:1.资料来浑日本海外电力调查会《海外电气事业统 计》和《中国电力统计资料》. 2.说明:(l)电力消费t系按电厂的发电t或净发电 t计算;(2)美国、日本、法国、英国系按供电热 效率计算煤耗，铭国、加幸大系按发电热效率计算 煤耗，中国则立接按发电煤耗计算;(3)发电能浑 消费(含火电、水电、核电等)均用上述计算的煤 耗乘以各自的总发电t。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条