1) Nickel monoxide
氧化亚镍
2) nickel hydroxide
氢氧化亚镍
1.
Determination of main contents and impurities of sphere nickel hydroxide by ICP-AES;
ICP-AES法测定球形氢氧化亚镍中的主成分及杂质
2.
Study on the relationship between structure and property of nickel hydroxide;
氢氧化亚镍的性能与结构之间关系的研究
3.
Spherical nickel hydroxide iq prepared by NH_3-coordinating liquid phasedeposition, and the bulk density and specific discharge capacity are also determinedMorphology and distribution are observed by means of SEM.
采用氨络合液相沉淀法制备出球氢氧化亚镍并检测了堆积密度和放电比容量。
3) nickel-nickel oxide
镍-氧化镍
1.
A modified electrode was fabricated by means of electrodeposition nickel-nickel oxide and copper-cuprous oxide on a glassy carbon electrode in the solution of Ni2+ and Cu2+.
在含镍离子和铜离子的溶液中用循环伏安法在玻碳电极(GCE)表面电化学沉积一层镍-氧化镍及铜-氧化亚铜纳米粒子(Ni/NiO、Cu/Cu2O),在-0。
4) spherical NiO fine particles
球形氧化亚镍微粉
5) nickel diiodide
碘化亚镍
6) nickel-nickel oxide film
镍-氧化镍膜
补充资料：氧化亚镍
NiO 分子量74．71
粉末状固体，色泽根据锻烧温度不同而至黑灰色或绿色。密度6.67g／cm3。熔点1990℃。溶于酸和氨水、热过氯酸、热硫酸，不溶于水、浓氨。空气中加热到400℃时，吸收氧变为三氧化二镍，600℃时又还原为氧化镍。经低温假烧制得的氧化镍具有化学活性。经1000℃高温煅烧制得的一氧化镍活性小，而且随制备温度的升高，密度和电阻增加，溶解度和催化活性降低。
应用领域 搪瓷工他用作瓷釉的密着剂和着色剂。陶瓷工业用作色料的原料。磁性材料生产中用作镍锌铁氧体的原料。玻璃工业用作茶色玻璃和显象管玻壳的着色剂。也是制造镍盐及镍催化剂的原料。
粉末状固体，色泽根据锻烧温度不同而至黑灰色或绿色。密度6.67g／cm3。熔点1990℃。溶于酸和氨水、热过氯酸、热硫酸，不溶于水、浓氨。空气中加热到400℃时，吸收氧变为三氧化二镍，600℃时又还原为氧化镍。经低温假烧制得的氧化镍具有化学活性。经1000℃高温煅烧制得的一氧化镍活性小，而且随制备温度的升高，密度和电阻增加，溶解度和催化活性降低。
应用领域 搪瓷工他用作瓷釉的密着剂和着色剂。陶瓷工业用作色料的原料。磁性材料生产中用作镍锌铁氧体的原料。玻璃工业用作茶色玻璃和显象管玻壳的着色剂。也是制造镍盐及镍催化剂的原料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。