1.
Recently high temperature protection coating is a focus technology on manufacture aeronautic turbine blade with excellent perfor- mance,whose basis is nickel-based directionally solidified superalloy.
发展高温防护涂层是近年来涡轮叶片制造技术的热点问题之一,针对当前航空发动机涡轮叶片的主要用材——镍基定向凝固合金,本文系统研究了室温和700℃高温条件下,表面高温防护涂层的存在对镍基定向凝固合金基体低周疲劳性能的影响。
6) directionally solidified Ni-base superalloy
定向凝固镍基高温合金
1.
The stress rupture performances of a directionally solidified Ni-base superalloy DZ951 have been investigated over a wide stress range of 50 to 970 MPa at high temperatures (650 to 1040 ℃).
研究了定向凝固镍基高温合金DZ951在广泛应力范围(50~970MPa)内的高温(650~1040℃)持久性能。
补充资料：快凝镍基合金
分子式：
CAS号：
性质：利用快速凝固技术制备的镍基合金。可以分成快凝镍基非晶合金和快凝镍基微晶合金两大类。快凝镍基非晶合金Ni-B，Ni-P，Ni-Si，Ni-Cr-B等是用熔液旋淬法制备的连续金属玻璃条带，厚度为30～40μm，可用于将不锈钢和镍基高温合金焊在一起的钎焊料。快凝镍基微晶合金主要用雾化法制备，其优点是组织细化和成分均匀，性能大幅度提高。如AF-115涡轮盘用快凝镍基合金的使用温度高于目前常用的Rene 95约100℃以上。急冷Ni-17％Al-9％～11％Mo合金的抗蠕变性能和抗氧化性能均比Mar-M200合金高85℃，是性能较好的镍基合金口十片材料，用于多层复合式涡轮机。