1) brittleness temperature
脆化点
2) brittle point
脆裂点，脆化点
3) asphalt embrittle point
沥青脆化点
4) brittle temperature test
脆化点试验
6) embrittlement
[em'britlmənt]
脆化
1.
This study is concerned with the effect of post welding heat treatment(PWHT)on the microstructure and properties at the intercritical reheated coarse-grained heat-affected zone(IRCGHAZ)of WB36 steel, and investigated whether the PWHT could reduce IRCGHAZ embrittlement.
针对WB36钢(15NiCuMoNb5)临界再热粗晶区(IRCGHAZ)存在的脆化现象,研究了焊后热处理对模拟临界再热粗晶区(IRCGHAZ)组织性能的影响,探讨其改善韧性作用。
2.
The embrittlement in 1Cr21Ni5Ti duplex stainles s steel with medium titanium and aluminum content, the temperature range in whic h the toughness is sharply deteriorated has been determined and effect of soluti on temperature has been researched.
针对中限钛、铝的Cr21Ni5Ti双相不锈钢中发现的脆化现象,探索了脆化发生的温度范围以及脆化与固溶温度的相关性。
3.
The study wanted to solve the embrittlement problem in copper alloy due to bismuth in drinking water pipe,The result showed that the embrittlement of copper alloy can be completely avoided when Sn and P were added,A proportion of Cu-Bi 1 Sn 3 Zn 6 P 0.
为了解决因铋的加入引起的铜合金脆化问题,研究结果表明,通过添加元素Sn、P完全解决了因铋引起的脆化问题,并提出了配方Cu Bi1Sn3Zn6P0。
补充资料：脆化点
分子式：
CAS号：
性质：又称脆化点。聚合物当温度降低至不能产生强迫高弹性而呈玻璃态，同时高弹性消失，产生脆性断裂时的临界温度，以Tb表示。Tb表征了塑料的耐寒性。Tb常用低温冲击压缩试验法测定，即在低温下，用一定速度的冲锤冲击压缩多个试样，测得试样破裂率为50%时的温度，即为Tb。由于试验结果的分散性，所以一般试验方法都人为规定试样中有50%脆化破裂时的温度。这一温度值是表明该种材料低温使用性能，有相对的比较意义。高分子的脆化温度本质上与玻璃化温度(Tg)相当，但测定方法不同。脆化温度测定方法有ASTMD 746，把规定尺寸的长方形试片浸入一定温度的冷介质中3min，用锤子以一定速度冲击，50%试片破坏时的温度为脆化温度。
CAS号：
性质：又称脆化点。聚合物当温度降低至不能产生强迫高弹性而呈玻璃态，同时高弹性消失，产生脆性断裂时的临界温度，以Tb表示。Tb表征了塑料的耐寒性。Tb常用低温冲击压缩试验法测定，即在低温下，用一定速度的冲锤冲击压缩多个试样，测得试样破裂率为50%时的温度，即为Tb。由于试验结果的分散性，所以一般试验方法都人为规定试样中有50%脆化破裂时的温度。这一温度值是表明该种材料低温使用性能，有相对的比较意义。高分子的脆化温度本质上与玻璃化温度(Tg)相当，但测定方法不同。脆化温度测定方法有ASTMD 746，把规定尺寸的长方形试片浸入一定温度的冷介质中3min，用锤子以一定速度冲击，50%试片破坏时的温度为脆化温度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。