1) methyl block RTV silicone rubber adhesive
嵌段甲基室温硫化硅橡胶黏合剂
2) RTV block methyl silicone rubber
甲基嵌段室温硫化硅橡胶
1.
Main factors affecting vulcanization time of RTV block methyl silicone rubber.;
影响甲基嵌段室温硫化硅橡胶硫化时间的主要因素
4) Siloxanes and silicones,dimethyl hydroxy-terminated
室温硫化甲基硅橡胶(107型)
5) room-temperature vulcanized silicone rubber
室温硫化硅橡胶
1.
Enhancing methods of room-temperature vulcanized silicone rubber adhesive;
室温硫化硅橡胶胶粘剂的增强方法
2.
With PDMS(polydimethyl siloxane)of appropriate viscosity as matrix and addition of appropriate fillers and assistants,the room-temperature vulcanized silicone rubber coatings was successfully prepared.
采用一定粘度的聚二甲基硅氧烷为基体,加入适量填料和助剂,成功制备了室温硫化硅橡胶涂层。
3.
With hydroxyl group terminated PDMS on both side as feedstock, adding several kinds of fillers and adjuvants, the room-temperature vulcanized silicone rubber coatings are prepared.
以二羟基聚二甲基硅氧烷(PDMS)为基体,加入不同填料和助剂,制备了室温硫化硅橡胶涂层。
6) room temperature vulcanized silicone rubber
室温硫化硅橡胶
1.
Modified room temperature vulcanized silicone rubber adhesive filled in situ with silica white;
白炭黑原位填充的改性室温硫化硅橡胶胶黏剂
2.
Research progress in thermal conductive room temperature vulcanized silicone rubber;
导热室温硫化硅橡胶的研究进展
3.
Progress in reinforcemnet and modification of room temperature vulcanized silicone rubber;
室温硫化硅橡胶的增强改性研究进展
补充资料：嵌段甲基室温硫化硅橡胶黏合剂
分子式：
CAS号：
性质：硫化前为流动的黏稠液到不流动的膏状物。硫化胶的拉伸强度4~6MPa，相对伸长率200%～500%，使用温度范围-60～200℃。由羟基封端的二甲基聚硅氧烷和甲基三乙氧基硅烷的低聚体以7：3或5：5的比例混合配制成胶料，配制时也可加入适量的气相法白炭黑。使用前，加入0.5%～2%的二丁基二月桂酸锡催化剂。硫化过程中发生嵌段共聚反应，提高了硅橡胶的强度。用作黏合剂、灌注料、密封、浸渍、印模及脱模材料。
CAS号：
性质：硫化前为流动的黏稠液到不流动的膏状物。硫化胶的拉伸强度4~6MPa，相对伸长率200%～500%，使用温度范围-60～200℃。由羟基封端的二甲基聚硅氧烷和甲基三乙氧基硅烷的低聚体以7：3或5：5的比例混合配制成胶料，配制时也可加入适量的气相法白炭黑。使用前，加入0.5%～2%的二丁基二月桂酸锡催化剂。硫化过程中发生嵌段共聚反应，提高了硅橡胶的强度。用作黏合剂、灌注料、密封、浸渍、印模及脱模材料。