1) firing curve
烧成曲线
2) baking curve
焙烧曲线
3) sintering curve
烧结曲线
1.
The influence of heating rate on the densities were studied through the observation of the sintering curves of α-Al_2O_3 green compacts with the mean grain size 300nm.
研究了平均粒径为300nm的-αAl2O3坯体的恒速烧结曲线,观察了升温速率对烧结密度的影响,得到了两种升温速率条件下,烧结体相对密度之差与温度的关系。
2.
The sintering curves showed that the sintering temperature of green body prepared by vacuum gel-casting was 100 ℃ lower than that of common gel-casting,and the contractive ratio of vacuum green body was 78.
烧结曲线表明,真空凝胶注模制得的坯体的烧结温度比普通凝胶注模制得的坯体的低100℃左右。
4) burning-off curve
燃烧曲线
5) master sintering curve
主烧结曲线
1.
Based on the combined-stage sintering model, the master sintering curve (MSC) for rutile TiO2 was constructed for sinter-ing in air with normal pressure and using constant a heating rate in a dilatometer.
采用纳米金红石相TiO2粉末在空气中进行烧结,用热膨胀仪记录恒定加热速率条件下的烧结过程,测量了烧结体密度,根据烧结3个阶段的全期烧结模型(combined-stage sintering model),建立TiO2主烧结曲线(master sintering curve)。
2.
The master sintering curve(MSC) of rutile of TiO2 was constructed using constant heating rate dilatometry data based on the combined-stages sintering model.
纳米金红石TiO2粉末在高温热膨胀仪中进行恒速无压烧结,升温速率为2℃/min和5℃/min,热膨胀仪自动记录烧结收缩量,根据全期烧结模型,建立TiO2主烧结曲线;利用阿基米德法测量烧结体的相对密度,利用扫描电镜观察烧结体在不同温度的显微组织演变。
3.
The master sintering curve(MSC) of 2.
5μm)主烧结曲线;利用主烧结曲线得到的相对密度和阿基米德法测得的烧结体(经过不同烧结制度)相对密度一致,说明主烧结曲线对烧结路径不敏感,烧结体的相对密度仅是时间和温度的函数,从而证明了所建主烧结曲线的有效性。
6) combustion diagram
燃烧曲线图
补充资料：烧成曲线
分子式：
CAS号：
性质：表示陶瓷坯体或砖瓦在烧成过程中温度随时间关系的曲线。通常由升温、保温和冷却三个阶段，至少由三段构成，复杂的烧成曲线可由10段以上（即10个以上的控温点）组成。能在最短的烧成周期获得合格的制品的烧成曲线称为最佳烧成曲线。合理的烧成曲线建立在对坯体在烧成过程中的物理-化学变化及产品尺寸有深刻的理解的基础上，同时是窑炉设计和温度制度的主要依据。
CAS号：
性质：表示陶瓷坯体或砖瓦在烧成过程中温度随时间关系的曲线。通常由升温、保温和冷却三个阶段，至少由三段构成，复杂的烧成曲线可由10段以上（即10个以上的控温点）组成。能在最短的烧成周期获得合格的制品的烧成曲线称为最佳烧成曲线。合理的烧成曲线建立在对坯体在烧成过程中的物理-化学变化及产品尺寸有深刻的理解的基础上，同时是窑炉设计和温度制度的主要依据。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。