1) crystal activity
晶体激活度
2) active crystalline material
激活晶体物质
3) crystal of high activity
易激晶体，高活性晶体
4) crystal of high activity
高活性晶体;易激晶体
5) activation energy
晶化激活能
1.
The experimental results show that the crystallization temperature( T p) and activation energy ( E c) of the crystalline phases ( α Fe and Sm 2Fe 17 C x ) can be decreased going through pre annealing, the trend of activation energy change of α Fe phase can be changed in the crystallization process, which is helpful to formati.
结果表明 ,预退火处理使非晶合金晶化相α Fe和Sm2 Fe17Cx 的晶化温度 (Tp)和晶化表观激活能(Ec)值降低 ,且改变晶化相α Fe在晶化过程中晶化激活能的变化趋势 ,有助于该合金在晶化退火中形成晶粒尺寸较小的α Fe相。
2.
The activation energy of glass transition,crystallization and peak crystallization are 390.
2kJ/mol、晶化激活能Ex为325。
6) crystallization activation energy
晶化激活能
1.
The crystallization activation energy has been calculated by DTA and Kissinger equation.
非晶态合金Fe78Si9B1 3样品经短时超短脉冲电流处理 ,发生了结构弛豫 ,用DTA方法及Kissinger方程计算非晶样品的晶化激活能 ,用穆斯堡尔谱学方法研究了试样在电脉冲处理后的无反冲分数的变化 。
2.
The apparent crystallization activation energy E, is calculated to be 471.
采用Kissinger和Doylle-Ozawa方法计算了表观晶化激活能E_a,分别为471。
3.
The crystallization activation energy calculated by the onset crystallization temperatures decreases obviously.
Nb使由初始晶化温度计算的晶化激活能明显降低。
补充资料：无公度晶体
分子式：
CAS号：
性质：不能按同一公共尺度去衡量，即不能用同一平移矢量使晶胞中全部粒子复原的晶体。无公度晶体的产生是因为某些微扰，使得晶体中出现的两套亚点阵结构的周期彼此存在微小差异而不能按同一平移矢量使晶体复原。
CAS号：
性质：不能按同一公共尺度去衡量，即不能用同一平移矢量使晶胞中全部粒子复原的晶体。无公度晶体的产生是因为某些微扰，使得晶体中出现的两套亚点阵结构的周期彼此存在微小差异而不能按同一平移矢量使晶体复原。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条