1) corrosion-resistant casing
抗蚀套管
2) Anti-CO2 corrosion casing
抗CO_2腐蚀套管
3) Development of anticorrosion casing
抗蚀套管开发
4) casing corrosion
套管腐蚀
1.
Effect of external stress to casing corrosion rate;
外应力对套管腐蚀速率的影响
2.
The casing corrosion is quite severe in CO_2 oil/gas wells with high temperature and pressure.
在高温高压含CO2油气井中,套管腐蚀是相当严重的,CO2腐蚀以点状(坑状)腐蚀为主,腐蚀的形状大多呈球窝形。
3.
The results showed that the for-mation water from Jingsha strata contains C02 is the main cause of casing corrosion in Huayuan Oilfield.
在了解花园油田套管腐蚀损坏状况后，我们在室内进行了地层水不含CO2及合CO2的腐蚀实验。
5) anti-squeeze casing
抗挤套管
1.
Furthermore, an anti-squeeze casing with high strength was developed and used in more than 600 wells.
为此,中原油田采用三维数值模拟方法研究盐岩层蠕变规律,并定量计算出作用在套管上的横向推挤力,在此基础上开发应用了抗外挤强度大于167MPa的非API高抗挤套管。
6) C90 anticorrosion oil tube
抗腐蚀油管
1.
Heat treatment process of C90 anticorrosion oil tube was established by test.
通过试验室电阻炉对C90抗腐蚀油管三种热处理方案进行对比试验,并就化学成分和热处理工艺对C90抗腐蚀油管性能方面的影响进行了简要论述,由此确定了C90抗腐蚀油管合适的热处理工艺,并用这一工艺应用于C90抗腐蚀油管合适的生产,取得了良好的效果。
补充资料：X射线抗蚀剂
分子式：
CAS号：
性质：采用软X射线（波长0.4～5nm）作为曝光源的抗蚀剂。由于X射线波长较紫外波长短两个数量级，几乎没有衍射的干扰，而且因其能量比电子束小得多，可以获得高分辨率，X射线对尘埃的透过性好，曝光工艺的缺陷率就低。所有的电子束抗蚀剂均可作X射线抗蚀剂。
CAS号：
性质：采用软X射线（波长0.4～5nm）作为曝光源的抗蚀剂。由于X射线波长较紫外波长短两个数量级，几乎没有衍射的干扰，而且因其能量比电子束小得多，可以获得高分辨率，X射线对尘埃的透过性好，曝光工艺的缺陷率就低。所有的电子束抗蚀剂均可作X射线抗蚀剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条