1) castable
可铸的
2) castable
可铸的，可塑的
4) malleable iron
可锻铸铁
1.
Study of retained austenite in the microstructure of austenitic-bainitic malleable iron;
奥-贝可锻铸铁组织中残余奥氏体的研究
2.
In order to optimize the heat treatment technology for pearlite malleable iron,experiment has been carried out on the basis of study on factors that have influence on the structure and properties of pearlitic malleable iron.
课题是对影响珠光体可锻铸铁组织及性能的因素进行研究,从而优化珠光体可锻铸铁热处理工艺。
3.
Based on the characteristic of malleable iron,the technology of multistage heat treatment formalleableiron was investigated successfully.
基于可锻铸铁的特点,成功开发了可锻铸铁多段加热热处理工艺。
5) Malleable Cast Iron
可锻铸铁
1.
Study on High Temperature Graphitizing Annealing Kinetics for High Manganese Malleable Cast Iron;
高锰可锻铸铁高温石墨化退火动力学研究
2.
Study of the fracture toughness of ductile cast iron (DCI) and malleable cast iron (MCI);
球墨铸铁和可锻铸铁的断裂韧性的研究
3.
The annealing process of malleable cast iron was improved by controlling the melting process.
针对可锻铸铁退火周期长,耗能大,退火后力学性能差的问题,通过熔炼工艺过程控制,改进退火工艺。
6) castability
可铸性
1.
07B, wt%) were studied using isothermal solidification method, the volume percent of solid and liquid of four alloys at different temperatures in the range between solidus and liquidus was measured and the effects of boron content on the solidification processes and castability of IC6 alloys were determined .
0 7wt% ) IC6合金理论上具有最佳可铸性。
2.
4%,precipitation temperature of eutectic(γ+γ′) decreases by 20℃,the range of solidus to liquidus are narrowed down obviously and castability of the alloy is improved greatly.
结果表明,低铝合金中(γ+γ′)共晶析出温度比高铝合金下降了20℃,液相线温度提高了5℃,并且失去枝晶间毛细补缩能力温度与固相线之间的温度范围明显缩小,失去枝晶间补缩区的液相量F明显减少,从而使低铝合金浇铸叶片时的热裂倾向降低,合金的可铸性提高。