1) low pressure polyethylene fibre
低压聚乙烯纤维
2) polyethylene fibre
聚乙烯纤维
1.
According to different molecular weight, the melt spinning, plasticized melt spinning, gel spinning and other non industrialized spinning methods of polyethylene fibres were reviewed.
综述纺制不同相对分子质量聚乙烯纤维的熔融纺丝法、增塑熔融纺丝法、冻胶纺丝法及其他一些非工业化的纺丝方法 ,并介绍了各种聚乙烯纤维性能和用途。
2.
Objective Polyethylene fibre coating with hydroxyapatite was used to strengthen a -TCP bone cement and improve its strength.
目的 采用羟基磷灰石包裹的聚乙烯纤维增强α-TCP生物骨水泥,以提高复合材料的强度。
3) polyethylene
[英][,pɔli'eθəli:n] [美]['pɑlɪ'ɛθəlin]
聚乙烯纤维
1.
Progress on Ultra-high Molecular Weight Polyethylene Fibers and Its Composites;
超高分子量聚乙烯纤维及其复合材料的研究进展
4) polyethylene fiber
聚乙烯纤维
1.
In vitro cytotoxicity of ultrahigh molecular weight polyethylene fiber;
超高相对分子质量聚乙烯纤维的体外细胞毒性
2.
Study on polyethylene fiber and poly-lactic acid complex in repairing of rabbit achilles tendon;
聚乙烯纤维-聚乳酸复合材料修复兔跟腱的研究
3.
Evaluation of biocompatibility of ultrahigh molecular weight polyethylene fiber;
超高相对分子质量聚乙烯纤维的生物相容性评价
补充资料：低压聚乙烯
结构式：[-CH2-CH2-]n
性状 无嗅、无味、无毒的白色颗粒或粉末。熔点13l℃。密度0．942-0．950g／cm3。软化点120-125℃。脆化温度-70℃。最高使用温度100℃。具有优良的耐热、耐寒、耐磨性及介电性、化学稳定性。在室温下几乎不溶于任何有机溶剂。能耐多种酸碱及各种盐类溶液的腐蚀。吸水性和水蒸气渗透性均低。但耐老化性能较差。
生产方法 主要采用泥浆法。在催化剂四氯化钛和一氯二乙基铝存在下，控制压力为〔1-5)×105Pa，温度65-75℃，将99％以上的乙烯，在溶剂汽油中聚合得到浆状物，再经醇解、中和、水洗、干燥、造粒而得。
拉仲屈服强度(MPa) ＞23．0
伸长率 (％) ＞200
冲击强度(kJ／m2) ＞9
维卡软化点(℃) >120
脆化温度(低温 冲击，℃)<70
体积电阻率(Ωcm) 1×1017
介电强度(kV／mm) ＞35
介电常数 2.35
介电损耗角正切 ＜5×10-4
应用领域 医药和化学工业用于制造中空制品，如桶、瓶及贮槽等。食品工业用于制造包装容器。机械工业用于：制造盖壳、手柄、手轮等通用机械零件，造纸工业用于制造合成纸。农业上用于制造覆盖薄膜。电气工业用于制造电缆绝缘及电气零部件。渔业上用于制造渔网。石油工业用于制造输水管及酸、减、盐等溶液输送管。