1) jarosite
['dʒærə,sait,dʒə'rəusit]
黄钾铁石
2) jarosite
['dʒærə,sait,dʒə'rəusit]
黄钾铁矾
1.
Biosynthesis and Characterization of Jarosite;
黄钾铁矾的生物合成与鉴定
2.
The formation conditions of jarosite and its environmental significance;
黄钾铁矾的形成条件研究及其环境意义
3.
The results indicate that both the precipitates produced by Leptospirillum ferriphium strain DY and Acidithiobacillus ferrooxidans strain GF are composed of jarosite and ammonium jarosite.
结果表明:无论是嗜铁钩端螺旋菌DY菌株(Leptospirillum ferriphium),还是嗜酸氧化亚铁硫杆菌GF菌株(Acidithiobacillus ferrooxidans)合成的沉淀都是黄钾铁矾和黄铵铁矾的混合物;其中,GF合成的沉淀混合物中黄钾铁矾的含量比DY合成的黄钾铁矾约高出5。
3) Jarosite process
黄钾铁矾法
1.
Jarosite process can obtain high recovery rate of zinc,simultaneously,most of indium remains in the jarosite residues and a little part of indium remains in the high acidities leaching residues.
某锌精矿中铟含量很高,采用黄钾铁矾法处理该高铟锌精矿,在得到较高锌回收率的同时,大部分的铟进入矾渣,少部分进入高浸渣,从矾渣和高浸渣中可回收得到电铟。
2.
Because of using zinc hydrometallurgy process of jarosite process, the leaching rate of zinc may reach 97% and this line can produce high quality zinc continuously and steadily.
采用黄钾铁矾法的湿法炼锌工艺 ,锌的浸出率可达到 97% ,可以稳定持续地生产优质锌。
3.
This paper covers production practice of jarosite process in hot acid leaching and comparison between iron hydroxide process and jarosite process that are used for iron removal.
介绍了热酸浸出黄钾铁矾工艺的生产实践 ,对氢氧化铁法和黄钾铁矾法两种除铁方法进行了比
4) jarosite rock
黄钾铁矾岩
5) spinel structure
铁钾尖晶石
1.
Iron catalyst containing potassium for dehydrogenation of ethylbenzene to styrene is a complex oxide catalyst with spinel structure.
用穆斯堡尔谱学和X射线衍射方法研究了使用过 2年的乙苯脱氢铁系催化剂及其在一定温度下进行再氧化处理的试样中铁化合物的组成和结构 ,着重研究了铁钾尖晶石结构 ,并与测量的催化参数进行对照。
6) iron-containing K-feldspar
含铁钾长石
1.
The NaX zeolite,synthesized from iron-containing K-feldspar powders,was studied with in situ high temperature X-ray diffraction.
对以含铁钾长石粉为原料、人工合成的NaX沸石分子筛,进行原位高温X射线衍射实验,实验结果表明:合成物中含有大量的非晶质,受热发生相变,在沸石表面结晶;沸石在800℃以下物相保持稳定,800~1 000℃发生相变,生成霞石、赤铁矿。
补充资料：黄钾铁矾
化学组成为KFe3[SO4]2(OH)6、晶体属三方晶系的硫酸盐矿物。部分钾常被钠类质同象代替，钠的原子数大于钾，称钠铁矾。晶体细小而罕见，呈板状或假菱面体状（实为两个三方单锥所构成的聚形）。玻璃光泽。具一组中等解理。摩斯硬度 2.5～3.5，比重 2.91～3.26。通常呈致密块状及隐晶质的土状、皮壳状集合体产生。赭黄色至暗褐色，条痕浅黄色。黄钾铁矾是干燥地区金属硫化物矿床氧化带中广泛分布的次生矿物，主要由黄铁矿因氧化分解而成。易于水解而成铁的氢氧化物，故常同褐铁矿等伴生。中国西北祁连山地区金属硫化物矿床氧化带上部,有大量的黄钾铁矾发育。质量纯净的,经煅烧后可作研磨粉的原料。