1) residualize
剩余场化
2) residual field
剩余场
3) residual curvature
剩余场曲
4) remnant polarization
剩余极化
1.
The highest remnant polarization 2Pr .
用溶胶-凝胶法制备了钛酸锶铋层状钙钛矿结构(SBTi)铁电陶瓷,研究了不同烧结温度对其显微结构和电性能的影响,分析了相关机理,发现1100℃烧结样品的晶粒发育比较完全,居里温度为520℃;压电常数d33和剩余极化强度2Pr较大,分别为9×10-12C/N和2。
2.
Under the electric filed of 125 kV/cm the remnant polarization (2P_(r)) of .
在测量电场强度为125kV/cm时,样品A和样品B的剩余极化(2Pr)分别为5。
3.
Vanadium-doping with appropriate content enlarges the remnant polarization (2P_ r ) and enhances the electric breakdown voltage of SrBi_ 4 Ti_ 4 O_ 15 (SBTi).
适量的钒掺杂,大大增加了SrBi4Ti4O15(SBTi)铁电材料的剩余极化2Pr,并改善了材料的耐压性能。
5) remanent polarization
剩余极化
1.
From the measurement of D-E hysteresis loops using RT6000HVS system,the remanent polarization and coercive field of SrBi 4Ti 4O 15 ceramic were found to be larger than 7μC/cm 2 and 73kV/cm respectively,and the sat.
对于SrBi4Ti4O1 5陶瓷施加 12 0kV cm的电场仍无法得到饱和的回线 ,此时的剩余极化和矫顽场分别约为 7μC cm2 和 73kV cm 。
2.
80)Ti_3O_(12)) films exhibited well-saturated polarization-electric field(P-E) switching curves with the remanent polarization(P_r) of 27 μC/cm~2 an.
80T i3O12薄膜具有较好电滞回线(P-E),在应用电压为10 V,测试频率为1MH z下,其剩余极化(Pr)及矫顽场(Ec)分别达到27μC/cm2和70 kV/cm。
3.
80 has the largest remanent polarization.
80时,薄膜具有最大的剩余极化(Pr),在应用电压为10V时,Pr及Ec分别达到27×10–6C/cm2和70×103V/cm。
6) residual culture
剩余文化
补充资料：剩余极化强度
分子式：
CAS号：
性质：铁电体经极化处理后，当撤除外电场后，其极化强度并不为零而是保持一有限值，称为剩余极化强度，常用Pr表示。表明已经定向排列的电畴在没有足够的反向电场输入附加能量，就无法回到其原来所处的随机状态。压电陶瓷因具有剩余极化才成为具有实用价值的压电元器件。
CAS号：
性质：铁电体经极化处理后，当撤除外电场后，其极化强度并不为零而是保持一有限值，称为剩余极化强度，常用Pr表示。表明已经定向排列的电畴在没有足够的反向电场输入附加能量，就无法回到其原来所处的随机状态。压电陶瓷因具有剩余极化才成为具有实用价值的压电元器件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。