1) saponified poly
皂化聚醋酸乙烯
2) saponified EVA adhe-sive
皂化乙烯-醋酸乙烯共聚体胶黏剂
3) PVAc
聚醋酸乙烯
1.
Synthesis of Low Polymerization Degree PVAc and the Rheologic Features of Reaction Liquid;
低聚合度聚醋酸乙烯合成与反应液流变特性
2.
Study on Preparation of Wall Brick from the BF Slags Containing Titania and the PVAC;
聚醋酸乙烯乳液制高炉渣墙体砖的研究
3.
In this experiment, by adding molecular adjustor and optimizing the experimental condition through orthogonal test, low molecular weight PVAc was firstly synthesized and then with NaOH as.
采用溶液聚合法,以醋酸乙烯为单体,偶氮二异丁腈为引发剂,甲醇为溶剂,加入分子量调节剂,通过多次实验优化实验条件,合成低相对分子质量的聚醋酸乙烯(PVAc),后者以NaOH为催化剂,经醇解得到了外观为白色粉末状、平均聚合度为600,醇解度为80%的低相对分子质量的PVA产品。
4) polyvinyl acetate
聚醋酸乙烯
1.
Study on the modified enviromental protection of polyvinyl acetate(PVAc) emulsion;
环保型聚醋酸乙烯酯乳液的改性研究
2.
Study on polyvinyl acetate emulsion modified by silicone;
有机硅改性聚醋酸乙烯乳液胶粘剂的研究
3.
Preparation of polyvinyl acetate/montmorillonite composite latex and it's property
聚醋酸乙烯/蒙脱土复合乳液的制备及性能
5) poly(vinyl acetate)
聚醋酸乙烯
1.
Using N,N,N′,N′-tetramethylethylenediamine and potassium persulphate as a redox initiation system,high molecular weight poly(vinyl acetate)(PVAc) was synthesized by aqueous deposited polymerization.
以N,N,N,′N′-四甲基乙二胺-过硫酸钾为氧化-还原引发体系,用水相沉淀聚合法合成了超高相对分子质量的聚醋酸乙烯(PVAc)。
6) polyvinul acetate gel
聚醋酸乙烯酸胶
补充资料：皂化乙烯-醋酸乙烯共聚体胶黏剂
分子式：
CAS号：
性质：由乙烯-醋酸乙烯共聚体部分或完全水解后生成的乙烯-醋酸乙烯-乙烯醇三元共聚体(EVAL)。其性质取决于三元单体的含量及分布、原料EVA树脂的性质。EVAL常用于四层和五层结构的阻气性复合膜。做食品、果汁、粉状化学品包装膜。还用于各种纤维织物的热熔黏合和涂层。对纤维有良好的粘接性能和耐水性、耐干洗性，在服装加工特别是妇女服装的加工生产方面广泛应用。皂化EVA还可做成粉末状热熔胶黏剂。
CAS号：
性质：由乙烯-醋酸乙烯共聚体部分或完全水解后生成的乙烯-醋酸乙烯-乙烯醇三元共聚体(EVAL)。其性质取决于三元单体的含量及分布、原料EVA树脂的性质。EVAL常用于四层和五层结构的阻气性复合膜。做食品、果汁、粉状化学品包装膜。还用于各种纤维织物的热熔黏合和涂层。对纤维有良好的粘接性能和耐水性、耐干洗性，在服装加工特别是妇女服装的加工生产方面广泛应用。皂化EVA还可做成粉末状热熔胶黏剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条