1) Spray distance
喷射距离
1.
Corrosion resistant of polyacrylate waterproof materials in the solution of chloride,sulfate and alkali was studied in static immersion,and relation between swelling ratio and anti-erosion of polymers formed by different initiators of spray distance and mass ratio was investigated.
通过溶胀度的测定,研究了不同喷射距离及不同质量分数引发剂所形成的聚合物溶胀度变化与抗侵蚀性关系。
2) Effective spraying range
有效喷射距离
3) spraying distance
喷涂距离
1.
Thermal barrier coatings were prepared by plasma spraying in different spraying distance,and through the tensile test of coating,XRD and SEM analysis,the influnce law of spraying distance on tensile strength(σ) of coating was investigated.
用等离子喷涂方法,在不同的喷涂距离(d)下制备出ZrO2陶瓷涂层,通过涂层的拉伸实验、X射线衍射和扫描电镜分析,研究了喷涂距离对涂层拉伸强度(σ)的影响规律。
2.
The effect of the spraying distance on the crystallization,surface morphology,electrical and optical properties of the films was investigated by X-ray diffraction,field emission scanning electron microscope,resistance tester and ultraviolet-visible spectrometer.
采用X射线衍射、场发射扫描电子显微镜、电阻仪、紫外-可见光谱仪等研究了喷涂距离(输入TiCl4管道末端到基板之间的距离)对沉积的TiN薄膜的结晶性能和表面形貌,以及薄膜的电学性能和光学性能的影响。
3.
During the wire electrical explosion,the coating feature is influenced by process variables such as input energy density,spraying distance.
为研究电爆喷涂工艺中输入能量密度及喷涂距离与喷涂效果之间的关系,利用高压电场中金属丝段与电极非接触电爆设备,通过改变金属丝长度和电极间电压进行系列金属丝段电爆喷涂试验,获得熔融粒子涂层、固态颗粒堆积涂层、气相沉积涂层及气相堆积涂层共4种涂层效果,其中熔融粒子涂层和气相沉积涂层具有工程应用价值。
4) spray distance
喷涂距离
1.
Experimental results indicate that proper spray distance,relatively larger arc-plasma current and voltage,comparatively lower powder feed rate can increase the microhardness and decrease the porosity of the coating;and thereby the optimized parameters are obtained.
通过正交试验方案分析了等离子喷涂主要工艺参数,即等离子弧电流、等离子弧电压、送粉率、喷涂距离,对NiCrBSi/Al2O3-TiO2涂层的显微硬度及孔隙度的影响,结合用光学显微镜对涂层显微形貌的观察和分析,得出的最佳工艺参数为电流I=600 A,电压U=55 V,送粉率F=15 g/min,喷涂距离S=10 cm;并且表明,采用适当的喷涂距离、较大的等离子弧电流和电压、较低的送粉率,可以提高涂层的显微硬度并降低其孔隙度。
2.
Hydroxyapatite (HA) coatings on Ti-6Al-4V substrate were prepared by atmospheric plasmasprating method under a variety of spray distances and spray powers.
本文以Ｔｉ－６Ａｌ－４Ｖ合金为基体材料，采用等离子喷涂方法，在不同喷涂距离和喷涂功率下制备羟基磷灰石（ＨＡ）涂层，研究喷涂距离和喷涂功率这两个重要的喷涂参数对涂层结构和组成的影响。
5) Distance of jet openings
喷口距离
补充资料：喷射
喷射
spray
喷射〔即阳y;ny皿.ep犯叫朋]，在微分流形M上的 切空间TM上的向量场W，用TM上与M的局部坐标(x’，…，丫)以自然的方式所伴随的局部坐标(x’，…，扩，vl，二，vn)表示，它的分量是(识，二，沪，.f’，…，f”)，其中尹二f‘(分，…，x”，。’，一，。”)是Cl类函数，并且对于固定的xl，…，扩创门是vl，…，扩的正的2次齐次函数(评的这些性质不依赖于局部坐标的实际选取).这个向量场决定的微分方程组 dx‘ —之创， dt 斋一f，(Xl，一，X·，一，…，。·)， 厄=l，二‘，n等价于2阶微分方程组 dZx，，，，。d无‘dx找、 二认于二f，〔x’，…，x”，气一，…厂号于》; d亡“、一”一’dt”dt/’因此，喷射(以不变的方式，即与坐标系无关的方式)描述了M上的这样一组微分方程. 喷射的最重要情形是厂‘为v’的2次多项式: j’‘二艺r{*(x’，二，x”)v，v女，r鑫，二r;*.(*)在此情形下，r{*在M上给出一个挠率为零的仿射联络(affine con议成ion).反过来，对于每一个仿射联络，测地线方程由某个喷射给出，其中f‘具有形状(*)(从联络过渡到喷射时，r;、关于下指标作对称化).如果向量场评是C，类的，则尹必定有(*)的形状.但是在一般情形下，W在丛TM的零截面的外部可以是光滑的，但是在这个截面附近不是CZ类的场.在这样一种情形下，人们有时谈论广义的喷射，而把“喷射”这一术语只留给特殊情形(*)使用.在Fi.招Ier几何学中测地线的微分方程产生了广义的喷射. 用不变的方式给出喷射的定义是可能的，它也适用于Banach流形(参见「1」).【补注】仿射联络的喷射也称为该联络的测地喷射(罗odesicsP功y).