2) UF resin
脲醛树脂胶
1.
An account is given of the requirements for equipment,adhesive,particle preparation,hot-pressing technology and testing methods when producing Grade E_1 particleboard with E_1 UF resin.
介绍在采用E_1级脲醛树脂胶的情况下,生产E_1级刨花板对设备、胶粘剂、刨花制备、热压工艺及检测的要求。
2.
This paper states that low quality raw material and improper technique proceeding are main factors of affecting product reserving property in preparing UF resin.
本文阐述了在制备脲醛树脂胶的过程中 ,质量较差的原材料和不当的工艺过程 ,是影响成品贮存性的主要因素 ,指出防止生产中出现凝胶等问题的措施。
3.
lt studies the structure and glue property of Salix mongolia, and low poison UF resin used in particleboard of Solix Mongolia.
通过试验分析了脲醛树脂胶中尿素与甲醛的摩尔比与树脂性能的关系；浓缩处理与树脂中游离甲醛含量的关系。
3) UF resin adhesive
脲醛树脂胶
1.
The effect of the molar ratio of formaldehyde to urea on the properties of UF resin adhesive and particleboard was investigated.
本文探讨了脲醛树脂胶中甲醛与尿素摩尔比(F/U)对胶粘剂和刨花板性能的影响,从而优选出生产E1级刨花板所用的胶粘剂。
2.
The paste formation of UF resin adhesive with low formaldehyde/urea molar ratio indicates the synthesis failure of the resin.
采用低摩尔比合成工艺的脲醛树脂胶产生糊化现象，原因在于加成反应阶段，因介质ｐＨ值低，生成了亚甲基脲不溶物，羟甲基化不能充分，它表明此次树脂胜的合成是失败的。
4) urea-formaldehyde resin adhesive
脲醛树脂胶
1.
Synthesis of environment protection type urea-formaldehyde resin adhesive;
环保型脲醛树脂胶的合成
2.
Development of the low cost urea-formaldehyde resin adhesive;
低成本脲醛树脂胶粘剂的研制
3.
The three main adhesives for artificial plate are urea-formaldehyde resin adhesive, phenolic-formaldehyde resin adhesive and melamine-formaldehyde resin adhensive.
人造板工业使用的三大胶是脲醛树脂胶、酚醛树脂胶和三聚氰胺-甲醛树脂胶。
5) urea formaldehyde resin adhesive
脲醛树脂胶
1.
The storing stability of urea formaldehyde resin adhesive with the change of PH value is researched in attempt to guide the production and imporove the application for products.
对脲醛树脂胶的贮存稳定性随 p H值的变化进行研究 ,以指导生产 ,提高产品的适用
补充资料：脲醛树脂
| 脲醛树脂 ure-aformaldehyde resins 尿素与甲醛反应得到的聚合物。又称脲甲醛树脂。英文缩写UF。加工成型时发生交联，制品为不溶不熔的热固性树脂。固化后的脲醛树脂颜色比酚醛树脂浅，呈半透明状，耐弱酸、弱碱，绝缘性能好，耐磨性极佳，价格便宜，但遇强酸、强碱易分解，耐候性较差。商品名Beetle。尿素与37％甲醛水溶液在酸或碱的催化下可缩聚得到线性脲醛低聚物，工业上以碱作催化剂，95℃左右反应，甲醛／尿素之摩尔比为1.5～2.0，以保证树脂能固化。反应第一步生成一和二羟甲基脲，然后羟甲基与氨基进一步缩合，得到可溶性树脂，如果用酸催化，易导致凝胶。产物需在中性条件下才能贮存。线性脲醛树脂以氯化铵为固化剂时可在室温固化。模塑粉则在130～160℃加热固化，促进剂如硫酸锌、磷酸三甲酯、草酸二乙酯等可加速固化过程。脲醛树脂主要用于制造模压塑料，制造日用生活品和电器零件，还可作板材粘合剂、纸和织物的浆料、贴面板、建筑装饰板等。由于其色浅和易于着色，制品往往色彩丰富瑰丽。 |