1) SiC Particle Agglomeration
SiC颗粒偏析
2) SiC particles
SiC颗粒
1.
The surface treatment of oxidation, acid-washing and acid-washing after oxidation were carried out on SiC particles, then 6066 aluminum alloy reinforced by SiC particles was fabricated by powder metallurgy route.
分别对SiC颗粒进行高温氧化、酸洗和高温氧化后再酸洗等表面处理,采用粉末冶金工艺制备了SiC颗粒增强的6066Al基复合材料。
2.
The initial research on bearing steel composites reinforced with 4%SiC particles by electro-slag melting and casting method have made.
用电冶熔铸的方法制备 4%SiC颗粒增强轴承钢复合材料 ,对其组织性能进行探索。
3.
Aluminum matrix composites reinforced with different volume fraction of SiC particles were manufactured by semi-solid casting in this thesis.
本文采用半固态复合铸造法制备了SiC颗粒增强铝基复合材料，并对这一系列材料的微观组织、硬度及耐磨性能进行了研究与分析。
3) SiC Particle
SiC颗粒
1.
Effect of pre-heating processing of SiC particles on porosity of SiC/Al composites;
SiC颗粒加热预处理工艺对SiC/Al复合材料制备的影响
2.
Study on the separation of the paramorphic SiC whisker and SiC particle;
同质异形体SiC晶须与SiC颗粒的分离
3.
The influence of SiC particles on grain structure development during laser rapid solidification;
SiC颗粒对Al-Zn合金激光快凝晶粒组织的影响
4) SiC particulates
SiC颗粒
1.
Copper matrix composites reinforced with SiC particulates were fabricated making use of powder metallurgy and hot extrusion processes.
结果表明,SiC颗粒作为增强相可以起到承载作用、减轻基体同偶件之间的粘着作用以及使基体产生塑性变形,从而显著改善复合材料的耐磨性能。
2.
The results show that the pretreatment of fibers hybridized withfine SiC particulates can improve not only the fiber distribution, but also the flexural property.
利用真空压力浸渗法制备了石墨纤维增强的铝基复合材料（Gr／ZL101A），研究了不同的纤维分布状态（SiC颗粒混杂纤维与未混杂的纤维）对复合材料显微组织及弯曲性能的影响。
5) SiC particulate
SiC颗粒
1.
Present condition and prospects of SiC particulate reinforced iron matrix composites;
SiC颗粒增强铁基复合材料的现状及展望
2.
Effects of SiC particulate on the properties of sintering iron matrix compostite;
SiC颗粒对烧结铁基复合材料性能的影响
3.
Mechanical properties of SiC particulate reinforced aluminum matrix composite sheets;
SiC颗粒增强铝基复合材料薄板的力学性能
6) β-SiC particulate
β-SiC颗粒
补充资料：Sic
1、名称解释
碳化硅又称金钢砂或耐火砂。碳化硅是用石英砂、石油焦(或煤焦)、木屑(生产绿色碳化硅时需要加食盐)等原料在电阻炉内经高温冶炼而成。目前我国工业生产的碳化硅分为黑色碳化硅和绿色碳化硅两种，均为六方晶体，比重为3.20～3.25，显微硬度为2840～3320kg/mm2。
包括黑碳化硅和绿碳化硅，其中：黑碳化硅是以石英砂,石油焦和优质硅石为主要原料,通过电阻炉高温冶炼而成。其硬度介于刚玉和金刚石之间,机械强度高于刚玉,性脆而锋利。绿碳化硅是以石油焦和优质硅石为主要原料,添加食盐作为添加剂，通过电阻炉高温冶炼而成。其硬度介于刚玉和金刚石之间,机械强度高于刚玉。
2.性质
碳化硅的硬度很大，具有优良的导热和导电性能，高温时能抗氧化。
3.用途
(1)作为磨料，可用来做磨具，如砂轮、油石、磨头、砂瓦类等。
(2)作为冶金脱氧剂和耐高温材料。
碳化硅主要有四大应用领域,即: 功能陶瓷、高级耐火材料、磨料及冶金原料。目前碳化硅粗料已能大量供应, 不能算高新技术产品,而技术含量极高 的纳米级碳化硅粉体的应用短时间不可能形成规模经济。
(3)高纯度的单晶，可用于制造半导体、制造碳化硅纤维。
4.产地、输往国别及品质规格
(1)产地：青海、宁夏、河南、四川、贵州等地。
(2)输往国别：美国、日本、韩国、及某些欧洲国家。
(3)品质规格：
①磨料级碳化硅技术条件按gb/t2480—96。各牌号的化学成分由表6-6-47和表6-6-48给出。
②磨料粒度及其组成按gb/t2477—83。磨料粒度组成测定方法按gb/t2481—83。