1.
CTOD Fracture Toughness Test for Weld Seam of Q370qE of Bridge
桥梁钢Q370qE焊缝断裂韧性CTOD试验研究
2.
"Providing good maintenance practices and correct weld parameter setting are done, no weld breaks are expected and no rewelds are necessary. "
只要维修良好,焊接工艺参数设定正确,不会出现焊缝断裂,不必重焊。
3.
Do not make a round trip jolty porch rail, lest the welding line of baluster bottom ruptures.
不要往返摇动阳台栏杆，以免栏杆底部的焊缝断裂。
4.
Fracture toughness of heat-affected zone( HAZ) was between the base metal and weld metal.
焊接热影响区的断裂韧性介于母材和焊缝金属之间。
5.
Fracture Analysis of Laser-Welded MW9124 Steel in Cold-Rolling Process and Study on Its Welding Technology;
MW9124硅钢带激光焊缝冷轧断裂分析及焊接工艺研究
6.
Thus the fracture likely initiated from fatigue sharpened cracks originating from slag and void in the plug welds.
因此，断裂可能是由于从塞焊焊缝内的焊渣和气孔外形成的尖锐的疲劳裂纹而产生的。
7.
Flux entrapped in the joints is the principal cause of low strength or failure.
裂缝中封存有焊药是强度不足或断裂的主要原因。
8.
The fracture features of Charpy impact test specimens of welded metal are also analyzed.
文中还对焊缝夏比冲击试样的断裂特性进行了探讨。
9.
The material fracture toughness was adequate to ensure development of the full fatigue resistance of the weld detail.
材料的断裂韧性可充分满足焊缝细节疲劳抗力的发挥。
10.
The electroslay welds were found to have a lower level of fracture toughness than implied from qualification tests.
人们发现电渣焊缝的断裂韧性较鉴定试验所给的结果要低。
11.
Addition of activating agent has no obvious effect on fracture toughness of weld metal.
添加活性剂对焊缝金属的断裂韧性没有明显作用。
12.
SCG Test on the Welding Joints of PE Gas Pipeline and Study on the Creep Fracture Parameters
聚乙烯燃气管道焊缝的SCG试验与蠕变断裂参量研究
13.
Inside Weld Crack Analysis and Control of SSAW Pipe
螺旋埋弧焊管内焊缝裂纹分析与控制
14.
Cause Analysis and Prevention Measure of Terminal Crack of Submerge-arc Welding Longtitudinal Weld
埋弧焊纵焊缝终端裂纹原因分析及预防措施
15.
However, ultrasonic checks showed cracks in the seams.
但是超声波检查，表明焊缝还有裂纹。
16.
The Analysis of Crystal Crack of T23 Waterwall Tube-fin
T23水冷壁管排鳍片焊缝裂纹的分析
17.
Cracking Analysis of Importation B70 Grade Line Welding Pipe in Cold-bend Test
进口B70级直缝焊管冷弯试验开裂分析
18.
The Repair in Welding Cracks on 20MnMoNi55 Low-alloy High-strength Steel
20MnMoNi55低合金高强钢焊缝裂纹的返修