1) nickel-base single crystal superalloy
镍基单晶合金
1.
The deformation and fracture characteristics of nickel-base single crystal superalloys at high temperatures, which are in plates with different thickness and in different crystallographic orientations, have been studied.
考察了镍基单晶合金DD3板试样在厚度为0。
2.
On the Meso-process of the rafting-derafting and coarsing of precipitate γ, a set of equations for creep deformation have been presented for nickel-base single crystal superalloys.
基于强化相γ′的筏化-解筏和粗化的细观过程,本文推导了一组用于描述镍基单晶合金蠕变变形过程的蠕变方程,并在950℃和760℃标定了国产DD3镍基单晶合金不同晶体取向的模型参数,与实验结果比较,所提模型可以准确地描述蠕变的主要阶段。
3) single crystal nickel-based superalloy
镍基单晶合金
1.
Low cycle fatigue damage is an important factor to effect the life of gas turbine blades made of single crystal nickel-based superalloy, but so far the many problems in this field are not deeply studied all over the world.
镍基单晶合金的低周疲劳损伤是影响镍基单晶合金涡轮叶片寿命的重要方面,但迄今为止国内外对这方面的许多问题还缺乏深入的研究。
4) nickel-based single crystal superalloy
镍基单晶合金
1.
Double shear creep specimen made of nickel-based single crystal superalloys can be loaded directly on its slip systems, i.
双剪切试样可以用来研究镍基单晶合金蠕变性能的晶体取向相关性。
5) Ni-based single crystal superalloy
镍基单晶合金
1.
Creep research of Ni-based single crystal superalloy: experiment,mechanism and material model
镍基单晶合金蠕变研究:试验、机理及材料模型
2.
Crystal-plasticity-based creep modelins for Ni-based single crystal superalloy
镍基单晶合金蠕变研究:基于晶体塑性的蠕变建模
6) single crystal nickel base superalloys
单晶镍基合金
1.
The affection factors of the creep behaviour for two single crystal nickel base superalloys with [001] orientation were studied by measuring the creep curves and internal stress of dislocation motion, and by EDAX composition analysis as well.
通过对 [0 0 1 ]取向单晶镍基合金蠕变曲线和位错运动内摩擦力的测定及能谱微区成分分析 ,研究了两种合金的蠕变特性。
补充资料：镍基单晶高温合金
镍基 单 晶 高温合金具有优良的高温性能，是目前制造先进航空发动机和燃气轮机叶片的主要材料。为了满足高性能航空发动机的设计需求，多年来，各国十分重视镍基单晶高温合金的研制和开发。20 世 纪 80年代以来，单晶高温合金一直沿着其独特的道路发展。随着合金设计理论水平的提高和生产工艺的改进，相继出现耐温能力比第1代单晶合金分别大约高30℃和60℃的第2代单晶合金和第3代单晶合金;第2代单晶高温合金的代表有pwa1484(') ,c msx一4(2).等，第3代单晶高温合金的代表有cmsx一loll',cm sx一11(0),r e nen6(5)等。研究表明[(6)，第3代单晶高温合金cmsx一10的耐温能力比第2代单晶合金cmsx -4(最高使用温度约(1163cc)的大约高3090，其使用温度可达1204℃左右，同时，还具有十分明显的蠕变强度优势。近年来出现的第4代单晶合金rr3010的承温能力达到11800c('1，用在英国rr公司最新研制的trent发动机上。re的加入以及hf,y ,la ,ru 等元素的合理应用，使新的单晶合金的持久性能和抗环境性能均有明显的提高。