1) ternary boride hard alloy
三元硼化物硬质合金
1.
A ternary boride hard alloy was prepared on Q235 steel substrate surface to form a new type of cladding material with ex-cellent wear and corrosion resistance by in situ reaction and liquid phase sintering in a vacuum furnace.
采用原位反应真空液相烧结技术,在Q235钢基体表面制备三元硼化物硬质合金覆层,使钢基体表面获得耐磨抗蚀、界面结合强度高的覆层材料。
2.
A ternary boride hard alloy was prepared on Q235 steel substrate surface to form a new type of cladding material with ex- cellent wear and corrosion resistance by in situ reaction and liquid phase sintering in a vacuum furnace.
采用原位反应真空液相烧结技术,在 Q235钢基体表面制备三元硼化物硬质合金覆层,使钢基体表面获得耐磨抗蚀、界面结合强度高的覆层材料。
4) ternary boride cermet
三元硼化物基金属陶瓷
1.
A ternary boride cermet clad material was fabricated on the Q235 steel substrate by means of the vacuum liquid phase sintering technique.
采用真空液相烧结法,在Q235钢表面制备三元硼化物基金属陶瓷覆层材料。
5) ternary boride
三元硼化物
1.
The research progress in the ternary boride base cermets within a few years is summarized.
总结了三元硼化物基金属陶瓷近几年的研究成果,主要论述了Mo2NiB2和Mo2FeB2基金属陶瓷的显微组织、合金元素的影响、制备技术以及性能的研究现状,总结了三元硼化物基金属陶瓷在刀具材料、模具材料以及覆层材料等领域的应用情况,并对今后的研究方向进行了展望。
2.
Using Mo powder,B—Fe alloy powder and Fe powder as raw materials,joined with Cr,Ni,C ingredient synchronously,ternary boride hard alloy clad materials are prepared on Q235 steel substrate by in situ reaction and vacuum liquid phase sintering technology.
以Mo粉、FeB合金粉和Fe粉为基本原料,同时加入Cr、Ni、C合金元素成分,采用原位反应真空液相烧结工艺,在Q235钢基体上制备三元硼化物基金属陶瓷覆层材料。
3.
Powder metallurgy HSS (PM HSS) is reinforced successfully at the temperature of 1193℃ using reaction sintering technology by composing with ternary boride based cermets.
采用反应硼化烧结法在1193℃下真空烧结,成功制备出具有良好耐磨性的粉末高速钢与三元硼化物陶瓷的复合材料;在自制摩擦磨损试验机上进行了摩擦磨损实验。
补充资料：硬硼钙石
分子式：Ca(H2O)[B2BO4(OH)3]
CAS号：
性质：硼矿的主要矿物组分之一。含三氧化二硼50.81%、氧化钙27.28%。单斜晶系，晶体呈短柱状或双锥状，集合体呈柱状、粒状、放射状、球状或块状。无色、乳白、浅黄、灰色等。玻璃光泽或强金刚光泽。硬度4.5，密度2.42g/cm3。不溶于水，易溶于热盐酸。燃烧时爆裂，脱落为鳞片状，火焰为绿色。产于炎热地区的干涸盐湖和温泉沉积中，常与石盐、天青石、石膏等共生。亦产于石膏岩和黏土岩中。是制取硼及硼化物的原料。
CAS号：
性质：硼矿的主要矿物组分之一。含三氧化二硼50.81%、氧化钙27.28%。单斜晶系，晶体呈短柱状或双锥状，集合体呈柱状、粒状、放射状、球状或块状。无色、乳白、浅黄、灰色等。玻璃光泽或强金刚光泽。硬度4.5，密度2.42g/cm3。不溶于水，易溶于热盐酸。燃烧时爆裂，脱落为鳞片状，火焰为绿色。产于炎热地区的干涸盐湖和温泉沉积中，常与石盐、天青石、石膏等共生。亦产于石膏岩和黏土岩中。是制取硼及硼化物的原料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条