3) Intumescent flame retardant
膨胀型阻燃
1.
Ammonium polyphosphate(APP)-pentaerythritol(PT)- melamine( M) systems have been chosen as an intumescent flame retardant(IFR),chlorination rubber as matrix resin to prepare flame resistant coating.
以多聚磷酸铵(APP)_季戊四醇(PT)_三聚氰胺(M)为膨胀型阻燃体系(IFR),氯化橡胶为基材树脂,制备阻燃涂料。
2.
The effect of the intumescent flame retardant system on ABS/PA6(80/20) alloys was studied.
以聚磷酸铵(APP)为酸源,利用ABS/PA6合金中PA6为炭源对ABS/PA6合金进行膨胀型阻燃研究,探讨了不同成炭协效剂与APP复配对合金阻燃性能的影响,这些成炭协效剂包括季戊四醇笼状磷酸酯(PEPA),热塑性酚醛树脂(TPPFR),环氧树脂(E-44)和分子筛4A。
4) flash fire retardant-type flame arrester
阻暴燃型阻火器
5) reactive flame retardant
反应型阻燃剂
1.
The new reactive flame retardant 2,4,6 tribromo N,N bis (2 hydroxylethyl) aniline was prepared with aniline, epoxy ethane and bromine as the raw materials.
以苯胺、环氧乙烷和溴素为原料 ,研究了新反应型阻燃剂 N,N-二 ( 2 -羟乙基 ) - 2 ,4,6-三溴苯胺的合成方法 ,用红外光谱和元素分析等方法确认了其化学结构。
6) intumescent fire retardant
膨胀型阻燃剂
1.
Polypropylene(PP) was fire retarded with a novel phosphorus,nitrogen and sulfur containing intumescent fire retardant(IFR),1,4-(O,O-diethyl thiophosphoryl imine) benzene (DTPB) which was synthesized by using phosphorus thiochloride,dehydrated alcohol and p-phenylenediamine.
以三氯硫磷、无水乙醇、对苯二胺为原料所合成的新型含磷、硫、氮的膨胀型阻燃剂(IFR),1,4-(O,O-二乙基硫代磷酰亚胺基)苯(DTPB)对聚丙烯(PP)进行阻燃,用热重法(TG)和差示扫描量热法(DSC)对阻燃PP的热性能进行了研究,利用氧指数仪测定了阻燃PP的极限氧指数(LOI)值,当阻燃剂含量为28%,LOI值为37。
2.
The typical system of intumescent fire retardant APP(ammonium polyphosphate) PER(pentaerythritol) was used to retard the combustion of low density polyethylene(LDPE) and the factors which influence the properties and the thermal degraded behaviour of intumescent fire retarded LDPE were discussed.
采用膨胀型阻燃剂—聚磷酸铵和季戊四醇 (APP/PER)体系对低密度聚乙烯 (LDPE)进行阻燃。
3.
The status of intumescent fire retardant developed was summaried by pentaerythritol and its derivatives, and heir the direction of development was prospected.
本文综述了以季戊四醇及其衍生物为炭源研制的膨胀型阻燃剂的发展状况,并对其今后的发展方向进行了展望。
补充资料：阻燃型双组分室温硫化硅橡胶
分子式：
CAS号：
性质：由聚二甲基硅氧烷、白炭黑组成。以聚二甲基硅氧烷与定量白炭黑和添加剂在混合器内混合，经碾磨均匀，包装成产品。本品为白色黏稠液。对金属无腐蚀性。硫化前具有较好流动性，硫化后拉伸强度2.54.0MPa，伸长率100%～150%。硬度(HA)45～55。阻燃性符合ULV-0级。用作电子元件的灌注包封材料，具有阻燃、防潮、绝缘、密封作用。
CAS号：
性质：由聚二甲基硅氧烷、白炭黑组成。以聚二甲基硅氧烷与定量白炭黑和添加剂在混合器内混合，经碾磨均匀，包装成产品。本品为白色黏稠液。对金属无腐蚀性。硫化前具有较好流动性，硫化后拉伸强度2.54.0MPa，伸长率100%～150%。硬度(HA)45～55。阻燃性符合ULV-0级。用作电子元件的灌注包封材料，具有阻燃、防潮、绝缘、密封作用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。