1) corundum castable
刚玉质浇注料
1.
Effect of nano-calcium carbonate addition on properties of corundum castable
纳米碳酸钙加入量对刚玉质浇注料性能的影响
2) corundum castables
刚玉浇注料
1.
This kind of refractory castables have good flow characteristics and excellent mechanical properties,and their hot rupture strength is better than that of ultra-low cement bonded corundum castables.
硅溶胶结合刚玉浇注料具有良好的流动性和常温强度,其高温热态抗折强度高于水泥结合刚玉浇注料。
2.
Corundum castables specimens were prepared by stirring 70 wt% tabular corundum grains,26 wt% tabular corundum fines and ultra-fines alumina,3 wt% pure calcium aluminate cement,1 wt% water-reducing agent and appropriate amount of water,pouring in the mold of vacuum casting equipment,beginning to vibrate when the vacuum degree reached 0,-0.
按板状刚玉颗粒70%(w)、板状刚玉细粉和氧化铝微粉26%(w)、纯铝酸钙水泥3%(w)和减水剂1%(w),加适量水配制成刚玉浇注料,搅拌均匀后倒入真空浇注设备的模具中,分别于真空度为0、-0。
3) Corundum-spinel castables
刚玉-尖晶石质浇注料
4) corundum based self-flow castable
刚玉质自流浇注料
1.
Influence of dispersant on fluidity of corundum based self-flow castable;
减水剂对刚玉质自流浇注料流变性能的影响
5) phosphate corundum refractory castables
磷酸刚玉质耐火浇注料
1.
Being as two layer refractory lining on valve plate and valve body,light mullite and phosphate corundum refractory castables are taken as heat isolation and heat resisting layers respectively.
阀板、阀体的耐火衬里隔热层采用莫来石轻质耐火浇注料、耐热层采用磷酸刚玉质耐火浇注料,进行两层浇注。
6) Corundum-magnesia castable
刚玉-MgO浇注料
补充资料：半透明烧结镁铝尖晶石陶瓷
分子式：
CAS号：
性质：又称半透明烧结镁铝尖晶石陶瓷。在0.3～6.5μm范围的线性光透射率大于10％，可见光范围的总透射率约为75％。用镁-铝的盐或氢氧化物的热分解产物为原料，添加少量烧结促进剂氧化钙等。在真空中经1800～1900℃或湿氢气氛中1700℃左右烧结成半透明陶瓷。可用于制作高温电弧、密封外壳、天线窗、红外透射装置等。
CAS号：
性质：又称半透明烧结镁铝尖晶石陶瓷。在0.3～6.5μm范围的线性光透射率大于10％，可见光范围的总透射率约为75％。用镁-铝的盐或氢氧化物的热分解产物为原料，添加少量烧结促进剂氧化钙等。在真空中经1800～1900℃或湿氢气氛中1700℃左右烧结成半透明陶瓷。可用于制作高温电弧、密封外壳、天线窗、红外透射装置等。